Compositions stabilized with substituted aminoxy silanes

ABSTRACT

Substituted aminoxy silane derivatives corresponding to the formula ##STR1## are effective in stabilizing organic materials against oxidative, thermal and actinic degradation, said derivatives being particularly effective as color improvers and process stabilizers in organic materials containing phenolic antioxidants and/or metal salts of fatty acids and/or hindered amine light stabilizers and/or organic phosphorus compounds.

Organic polymeric materials such as plastics and resins are subject to thermal, oxidative and photodegradation. A great variety of stabilizers are known in the art for stabilizing a diversity of substrates. Their effectiveness varies depending upon the causes of degradation and the substrate stabilized. In general, it is difficult to predict which stabilizer will be most effective and most economical for any one area of application. For example, stabilizer effectiveness in reducing volatility may depend upon preventing bond scission in the substrate molecule. Limiting embrittlement and retaining elasticity in a polymer or rubber may require prevention of excessive crosslinking and/or chain scission. Prevention of discoloration may require inhibiting reactions which yield new chromophores or color bodies in the substrate or stabilizer. Problems of process stability and incompatibility must also be considered.

Regarding the instant invention many aminoxy silanes have been disclosed in U.S. Pat. No. 3,448,136 use as end blockers in silicone chemistry and in the preparation of resins having potential as components of metal protectants. Pande et al, Chem. Ind. (London) 56 (1970) describe the preparation of (CH₃)_(n) Si(ONC₂ H₅)_(4-n) with n=0-3, absent a utility statement. Beckett et al, J. Pharm. Pharmac., 27, 659 (1975) describe the preparation of (C₆ H₅ CH₂)₂ NOSi(CH₃)₃ in conjunction with the study of the metabolism of dibenzylamine.

It has now been determined that the compositions of this invention exhibit a variety of desirable properties stemming from the presence therein of the indicated substituted aminoxy silanes. Thus, the compounds serve to protect various substrates such as polyolefins, elastomers and lubricating oils against the adverse effects of oxidative and thermal degradation. They are most effective as color improvers and process stabilizers in polyolefin compositions which may contain metal salts of fatty acids and which also contain a phenolic antioxidant. Thus, they serve to substantially reduce color formation resulting from the presence of the phenolic antioxidant and/or from the processing conditions as well as to directly protect the polymer from said processing conditions. They also prevent the discoloration of polyolefin compositions containing hindered amine light stabilizers or combinations of phenolic antioxidants and organic phosphites. In addition, the gas fading that may be experienced upon exposure to the combustion products of natural gas is also significantly reduced.

It is a primary object of this invention to provide compositions of organic materials stabilized against oxidative, thermal and actinic degradation by the presence therein of a class of substituted aminoxy silane derivatives.

It is a further object to provide such compositions which also contain phenolic antioxidants wherein said silanes substantially reduce color formation resulting from the presence of said phenol.

Various other objects and advantages of this invention will become evident from the following description thereof.

The stabilizing compounds utilized in the compositions of this invention correspond to the formula ##STR2## wherein

n is 0-4; and

R, R^(l) and R² are independently hydrogen, alkyl of 1 to 36 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, aralkyl of 7 to 9 carbon atoms or said aralkyl substituted by alkyl of 1 to 36 carbon atoms.

The R^(l) and R² groups are preferably hydrogen, straight-chain or branched alkyl with 1 to 18 carbon atoms such as methyl, ethyl, n-propyl, n-butyl, tert-butyl, n-pentyl, n-octyl, 2-ethylhexyl, decyl, dodecyl and octadecyl; cyclopentyl and cyclohexyl; and benzyl, α-methylbenzyl and α,α-dimethylbenzyl. R is preferably alkyl of 1 to 18 carbon atoms.

A procedure for preparing these silanes is disclosed in U.S. Pat. No. 3,448,136. In general, the procedure involves reacting the appropriately substituted hydroxylamine with the appropriately substitute halosilane in a solvent to yield the desired product. Typical halosilanes include silicon tetrachloride, dimethyldichlorosilane, methyltrichlorosilane, trimethylchlorosilane, methyl-hydrogen-dichlorosilane, and the like. The solvent can be, for example, heptane, cyclohexane, ether, benzene, toluene, xylene, methylene chloride, and the like. The reaction temperature ranges from 25° to 140° C. It is preferred to conduct the reaction in the presence of a proton acceptor such as triethylamine or pyridine.

An alternate approach involves reacting the substituted hydroxylamine with the appropriately substituted silyl trihaloacetamide in the presence of a solvent such as acetonitrile. The reaction temperature ranges from 25° to 80° C.

The starting materials needed to prepare the silanes are items of commerce or can be prepared by known methods.

The compounds used in the present invention are particularly effective in stabilizing organic materials subject to oxidative, thermal and actinic degradation, such as plastics, polymers and resins.

Substrates in which these compounds are particularly useful are polyolefins such as polyethylene and polypropylene; polystyrene, including impact polystyrene, ABS resin, SBR, isoprene, as well as natural rubber, polyesters including polyethylene terephthalate and polybutylene terephthalate, including copolymers, and lubricating oils such as those derived from mineral oil.

In general polymers which can be stabilized include

1. Polymers of monoolefins and diolefins, for example polyethylene (which optionally can be crosslinked), polypropylene, polyisobutylene, polybutene-1, polymethylpentene-1, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for instance of cyclopentene or norbornene.

2. Mixtures of the polymers mentioned under (1), for example mixtures of polypropylene with polyisobutylene.

3. Copolymers of monoolefins and diolefins with each other or with other vinyl monomers, such as, for example, ethylene/propylene, propylene/butene-1, propylene/isobutylene, ethylene/butene-1, propylene/butadiene, isobutylene/isoprene, ethylene/alkyl acrylates, ethylene/alkyl methacrylates, ethylene/vinyl acetate or ethylene/acrylic acid copolymers and their salts (ionomers) and terpolymers of ethylene with propylene and a diene, such as hexadiene, dicyclopentadiene or ethylidene-norbornene.

4. Polystyrene, poly-(p-methylstyrene).

5. Copolymers of styrene or methylstyrene with dienes or acrylic derivatives, such as styrene/butadiene, styrene/acrylonitrile, styrene/ethyl methacrylate, styrene/butadiene/ethyl acrylate, styrene/acrylonitrile/methyl acrylate; mixtures of high impact strength from styrene copolymers and another polymer, such as, for example, from a polyacrylate, a diene polymer or an ethylene/propylene/diene terpolymer; and block polymers of styrene, such as, for example, styrene/butadiene/styrene, styrene/isoprene/styrene, styrene/ethylene/butylene/styrene or styrene/ethylene/propylene/styrene.

6. Graft copolymers of styrene, such as, for example, styrene on polybutadiene, styrene and acrylonitrile on polybutadiene, styrene and alkyl acrylates or methacrylates on polybutadiene, styrene and acrylonitrile on ethylene/propylene/diene terpolymers, styrene and acrylonitrile on polyacrylates or polymethacrylates, styrene and acrylonitrile on acrylate/butadiene copolymers, as well as mixtures thereof with the copolymers listed under (5), for instance the copolymer mixtures known as ABS-, MBS-, ASA- or AES-polymers.

7. Halogen-containing polymers, such as polychloroprene, chlorinated rubbers, chlorinated or sulfochlorinated polyethylene, epichlorohydrin homo- and copolymers, polymers from halogen-containing vinyl compounds, as for example, polyvinylchloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride, as well as copolymers thereof, as for example, vinyl chloride/vinylidene chloride, vinyl chloride/vinyl acetate or vinylidene chloride/vinyl acetate copolymers.

8. Polymers which are derived from α,β-unsaturated acids and derivatives thereof, such as polyacrylates and polymethacrylates, polyacrylamide and polyacrylonitrile.

9. Copolymers from the monomers mentioned under (8) with each other or with other unsaturated monomers, such as, for instance, acrylonitrile/butadiene, acrylonitrile/alkyl acrylate, acrylonitrile/alkoxyalkyl acrylate or acryloacrylate, nitrile/vinyl halogenide copolymers or acrylonitrile/alkyl methacrylate/butadiene terpolymers.

10. Polymers which are derived from unsaturated alcohols and amines, or acyl derivatives thereof or acetals thereof, such as polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinylbutyral, polyallyl phthalate or polyallyl-melamine.

11. Homopolymers and copolymers of cyclic ethers, such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bis-glycidyl ethers.

12. Polyacetals, such as polyoxymethylene and those polyoxymethylenes which contain ethylene oxide as comonomer.

13. Polyphenylene oxides and sulfides, and mixtures of polyphenylene oxides with polystyrene.

14. Polyurethanes which are derived from polyethers, polyesters or polybutadienes with terminal hydroxyl groups on the one side and aliphatic or aromatic polyisocyanates on the other side, as well as precursors thereof (polyisocyanates, polyols or prepolymers).

15. Polyamides and copolyamides which are derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, such as polyamide 4, polyamide 6, polyamide 6/6, polyamide 6/10, polyamide 11, polyamide 12, poly-2,4,4-trimethylhexamethylene terephthalamide or poly-m-phenylene isophthalamide, as well as copolymers thereof with polyethers, such as for instance with polyethylene glycol, polypropylene glycol or polytetramethylene glycols.

16. Polyureas, polyimides and polyamide-imides.

17. Polyesters which are derived from dicarboxylic acids and diols and/or from hydroxycarboxylic acids or the corresponding lactones, such as polyethylene terephthalate, polybutylene terephthalate, poly-1,4-dimethylol-cyclohexane terephthalate, poly-[2,2-(4-hydroxyphenyl)-propane] terephthalate and polyhydroxybenzoates as well as block-copolyether-esters derived from polyethers having hydroxyl end groups.

18. Polycarbonates.

19. Polysulfones, polyethersulfones and polyetherketones.

20. Crosslinked polymers which are derived from aldehydes on the one hand and phenols, ureas and melamines on the other hand, such as phenol/formaldehyde resins, urea/formaldehyde resins and melamine/formaldehyde resins.

21. Drying and non-drying alkyd resins.

22. Unsaturated polyester resins which are derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and vinyl compounds as crosslinking agents, and also halogen-containing modifications thereof of low flammability.

23. Thermosetting acrylic resins, derived from substituted acrylic esters, such as epoxy-acrylates, urethane-acrylates or polyester acrylates.

24. Alkyd resins, polyester resins or acrylate resins in admixture with melamine resins, urea resins, polyisocyanates or epoxide resins as crosslinking agents.

25. Crosslinked epoxide resins which are derived from polyepoxides, for example from bis-glycidyl ethers or from cycloaliphatic diepoxides.

26. Natural polymers, such as cellulose, rubber, gelatin and derivatives thereof which are chemically modified in a polymer homologous manner, such as cellulose acetates, cellulose propionates and cellulose butyrates, or the cellulose ethers, such as methylcellulose.

27. Mixtures of polymers as mentioned above, for example PP/EPDM, Polyamide 6/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS.

28. Naturally occuring and synthetic organic materials which are pure monomeric compounds or mixtures of such compounds, for example mineral oils, animal and vegetable fats, oil and waxes, or oils, fats and waxes based on synthetic esters (e.g. phthalates, adipates, phosphates or trimellitates) and also mixtures of synthetic esters with mineral oils in any weight ratios, which materials may be used as plasticizers for polymers or as textile spinning oils, as well as aqueous emulsions of such materials.

29. Aqueous emulsions of natural or synthetic rubber, e.g. natural latex or latices of carboxylated styrene/butadiene copolymers.

In general, the compounds of the present invention are employed in from about 0.01 to about 5% by weight of the stabilized composition, although this will vary with the particular substrate and application. An advantageous range is from about 0.5 to about 2%, and especially 0.1 to about 1%.

The stabilizers of the instant invention may readily be incorporated into the organic polymers by conventional techniques, at any convenient stage prior to the manufacture of shaped articles therefrom. For example, the stabilizer may be mixed with the polymer in dry powder form, or a suspension or emulsion of the stabilizer may be mixed with a solution, suspension, or emulsion of the polymer. The resulting stabilized polymer compositions of the invention may optionally also contain various conventional additives, such as the following.

1. Antioxidants

1.1. Alkylated monophenols, for example,

2,6-di-tert.butyl-4-methylphenol

2-tert.butyl-4,6-dimethylphenol

2,6-di-tert.butyl-4-ethylphenol

2,6-di-tert.butyl-4-n-butylphenol

2,6-di-tert.butyl-4-i-butylphenol

2,6-di-cyclopentyl-4-methylphenol

2-(α-methylcyclohexyl)-4,6-dimethylphenol

2,6-di-octadecyl-4-methylphenol

2,4,6-tri-cyclohexylphenol

2,6-di-tert.butyl-4-methoxymethylphenol

1.2. Alkylated hydroquinones, for example,

2,6-di-tert.butyl-4-methoxyphenol

2,5-di-tert.butyl-hydroquinone

2,5-di-tert.amyl-hydroquinone

2,6-diphenyl-4-octadecyloxyphenol

1.3. Hydroxylated thiodiphenyl ethers, for example,

2,2'-thio-bis-(6-tert.butyl-4-methylphenol)

2,2'-thio-bis-(4-octylphenol)

4,4'-thio-bis-(6-tert.butyl-3-methylphenol)

4,4'-thio-bis-(6-tert.butyl-2-methylphenol)

1.4. Alkyliden-bisphenols, for example,

2,2'-methylene-bis-(6-tert.butyl-4-methylphenol)

2,2'-methylene-bis-(6-tert.butyl-4-ethylphenol)

2,2'-methylene-bis-[4-methyl-6-(α-methylcyclohexyl)-phenol]

2,2'-methylene-bis-(4-methyl-6-cyclohexylphenol)

2,2'-methylene-bis-(6-nonyl-4-methylphenol)

2,2'-methylene-bis-[6-(α-methylbenzyl)-4-nonylphenol]

2,2'-methylene-bis-[6-(α,α-dimethylbenzyl)-4-nonylphenol]

2,2'-methylene-bis-(4,6-di-tert.butylphenol)

2,2'-ethylidene-bis-(4,6-di-tert.butylphenol)

2,2'-ethylidene-bis-(6-tert.butyl-4-isobutylphenol)

4,4'-methylene-bis-(2,6-di-tert.butylphenol)

4,4'-methylene-bis-(6-tert.butyl-2-methylphenol)

1,1-bis-(5-tert.butyl-4-hydroxy-2-methylphenyl-butane)

2,6-di-(3-tert.butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol

1,1,3-tris-(5-tert.butyl-4-hydroxy-2-methylphenyl)-butane

1,1-bis-(5-tert.butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane

ethyleneglycol-bis-[3,3-bis-(3'-tert.butyl-4'-hydroxyphenyl)-butyrate]

di-(3-tert.butyl-4-hydroxy-5-methylphenyl)-dicyclopentadiene

di-[2-(3'-tert.butyl-2'-hydroxy-5'-methyl-benz-yl)-6-tert.-butyl-4-methylphenyl]-terephthalate.

1.5. Benzyl compounds, for example,

1,3,5-tri-(3,5-di-tert.butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene-di-(3,5-di-tert.butyl-4-hydroxybenzyl)sulfide

3,5-di-tert.butyl-4-hydroxybenzyl-mercapto-acetic acid isooctyl ester

bis-(4-tert.butyl-3-hydroxy-2,6-dimethylbenzyl)dithiolterephthalate

1,3,5-tris-(3,5-di-tert.butyl-4-hydroxybenzyl)isocyanurate

1,3,5-tris-(4-tert.butyl-3hydroxy-2,6-dimethylbenzyl)isocyanurate

3,5-di-tert.butyl-4-hydroxybenzyl-phosphoric acid-dioctadecyl ester

3,5-di-tert.butyl-4-hydroxybenzyl-phosphoric acid-monoethyl ester, calcium-salt

1.6. Acylaminophenols, for example,

4-hydroxy-lauric acid anilide

4-hydroxy-stearic acid anilide

2,4-bis-octylmercapto-6-(3,5-tert.butyl-4-hydroxyanilino)-s-triazine

octyl-N-(3,5-di-tert.butyl-4-hydroxyphenyl)-carbamate

1.7. Esters of β-(3,5-di-tert.butyl-4-hydroxyphenyl)propionic acid with monohydric or polyhydric alcohols, for example,

methanol

diethyleneglycol

octadecanol

triethyleneglycol

1,6-hexanediol

pentaerythritol

neopentylglycol

tris-hydroxyethyl isocyanurate

thiodiethyleneglycol

di-hydroxyethyl oxalic acid diamide

1.8. Esters of β-(5-tert.butyl-4-hydroxy-3-methylphenyl)propionic acid with monohydric or polyhydric alcohols, for example,

methanol

diethyleneglycol

octadecanol

triethyleneglycol

1,6-hexanediol

pentaerythritol

neopentylglycol

tris-hydroxyethyl isocyanurate

thiodiethyleneglycol

di-hydroxyethyl oxalic acid diamide

1.9. Amides of β-(3,5-di-tert.butyl-4-hydroxyphenyl)propionic acid for example,

N,N'-di-(3,5-di-tert.butyl-4-hydroxyphenylpropionyl)hexamethylendiamine

N,N'-di-(3,5-di-tert.butyl-4-hydroxyphenylpropionyl)trimethylendiamine

N,N'-di-(3,5-di-tert.butyl-4-hydroxyphenylpropionyl)hydrazine

2. UV absorbers and light stabilizers

2.1. 2-(2'-Hydroxyphenyl)-benzotriazoles, for example, the 5'-methyl-, 3',5'-di-tert.butyl-, 5'-tert.butyl-, 5'-(1,1,3,3-tetramethylbutyl)-, 5-chloro-3',5'-di-tert.-butyl-, 5-chloro-3'-tert.butyl-5'-methyl-, 3'-sec.butyl-5'-tert.butyl-, 4'-octoxy, 3',5'-di-tert.amyl-, 3',5'-bis-(α,α-dimethylbenzyl)-derivatives.

2.2. 2-Hydroxy-benzophenones, for example, the 4-hydroxy-, 4-methoxy-, 4-octoxy, 4-decyloxy-, 4-dodecyloxy-, 4-benzyloxy, 4,2',4'-trihydroxy- and 2'-hydroxy-4,4'-dimethoxy derivatives.

2.3. Esters of optionally substituted benzoic acids for example, phenyl salicylate, 4-tert.butyl-phenylsalicylate, octylphenyl salicylate, dibenzoylresorcinol, bis-(4-tert.-butylbenzoyl)-resorcinol, benzoylresorcinol, 3,5-di-tert.-butyl-4-hydroxybenzoic acid 2,4-di-tert.butyl-phenyl ester and 3,5-di-tert.-butyl-4-hydroxybenzoic acid hexadecyl ester.

2.4. Acrylates, for example, α-cyano-β,β-diphenylacrylic acid ethyl ester or isooctyl ester, α-carbomethoxy-cinnamic acid methyl ester, α-cyano-β-methyl-p-methoxy-cinnamic acid methyl ester or butyl ester, α-carbomethoxy-p-methoxycinnamic acid methyl ester, N-(β-carbomethoxy-β-cyanovinyl)-2-methyl-indoline.

2.5 Nickel compounds, for example, nickel complexes of 2,2'-thio-bis-[4-(1,1,3,3-tetramethylbutyl)-phenol], such as the 1:1 or.1:2 complex, optionally with additional ligands such as n-butylamine, triethanolamine or N-cyclohexyl-di-ethanolamine, nickel dibutyldithiocarbamate, nickel salts of 4-hydroxy-3,5-di-tert.butylbenzylphosphonic acid monoalkyl esters, such as of the methyl, ethyl or butyl ester, nickel complexes of ketoximes such as of 2-hydroxy-4-methyl-phenyl undecyl ketoxime, nickel complexes of 1-phenyl-4-lauroyl-5-hydroxy-pyrazol, optionally with additional ligands.

2.6. Sterically hindered amines, for example bis-(2,2,6,6-tetramethylpiperidyl)-sebacate, bis-(1,2,2,6,6-pentamethylpiperidyl)-sebacate, n-butyl-3,5-di-tert.butyl-4-hydroxybenzyl malonic acid bis-(1,2,2,6,6-pentamethylpiperidyl)ester, condensation product of 1-hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, condensation product of N,N'-(2,2,6,6-tetramethylpiperidyl)-hexamethylendiamine and 4-tert.octylamino-2,6-dichloro-1,3,5-s-triazine, tris-(2,2,6,6-tetramethylpiperidyl)-nitrilotriacetate, tetrakis-(2,2,6,6-tetramethyl-4-piperidyl)-1,2,3,4-butanetetracarbonic acid, 1,1'(1,2-ethanediyl)-bis-(3,3,5,5-tetramethylpiperazinone).

2.7. Oxalic acid diamides, for example, 4,4'-di-octyloxyoxanilide, 2,2'-di-octyloxy-5,5'-di-tert.butyl-oxanilide, 2,2'-di-dodecyloxy-5,5'-di-tert.butyl-oxanilide, 2-ethoxy-2'-ethyl-oxanilide, N,N'-bis (3-dimethylaminopropyl)oxalamide, 2-ethoxy-5-tert.butyl-2'-ethyloxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert.butyloxanilide and mixtures of ortho- and para-methoxy-as well as of o- and p-ethoxy-disubstituted oxanilides.

3. Metal deactivators, for example, N,N'-diphenyloxalic acid diamide, N-salicylal-N'-salicyloylhydrazine, N,N'-bis-salicyloylhydrazine, N,N'-bis-(3,5-di-tert.butyl-4-hydroxyphenylpropionyl)-hydrazine, 3-salicyloylamino-1,2,4-triazole, bis-benzylidene-oxalic acid dihydrazide.

4. Phosphites and phosphonites, for example, triphenyl phosphite, diphenylalkyl phosphites, phenyldialkyl phosphites, tri-(nonylphenyl)phosphite, trilauryl phosphite, trioctadecyl phosphite, di-stearyl-pentaerythritol diphosphite, tris-(2,4-di-tert.butylphenyl) phosphite, di-isodecylpentaerythritol diphosphite, di-(2,4-di-tert.-butylphenyl)pentaerythritol diphosphite, tristearyl-sorbitol triphosphite, tetrakis-(2,4-di-tert.butylphenyl)-4,4'-diphenylylenediphosphonite.

5. Compounds which destroy peroxide, for example, esters of β-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercapto-benzimidazole or the zinc salt of 2-mercaptobenzimidazole, zinc-dibutyl-dithiocarbamate, dioctadecyldisulfide, pentaerythritol-tetrakis(β-dodecylmercapto)-propionate.

6. Polyamide stabilizers, for example copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese.

7. Basic co-stabilizers, for example, melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids for example Ca stearate, Zn stearate, Mg stearate, Na ricinoleate and K palmitate, antimony pyrocatecholate or zinc pyrocatecholate.

8. Nucleating agents, for example, 4-tert.butyl-benzoic acid, adipic acid, diphenylacetic acid.

9. Fillers and reinforcing agents, for example, calcium carbonate, silicates, glass fibers, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite.

10. Other additives, for example, plasticizers, lubricants, emulsifiers, pigments, optical brighteners, flameproofing agents, anti-static agents, blowing agents and thiosynergists such as dilaurylthiodipropionate or distearylthiodipropionate.

While the instant aminoxy silanes can be beneficially used as stablizers for a variety of substrates, particularly the polyolefins, both alone and in conjunction with other coadditives, the introduction of the instant aminoxy silanes into polyolefins, optionally containing various alkali metal, alkaline earth metal and aluminum salts of higher fatty acids (see Additive #7 hereinabove), with hindered phenolic antioxidants exhibits enhanced and particularly salubrious protection to such substrates in terms of reducing color formation stemming from the presence of the phenols. Such phenolic antioxidants include n-octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, neopentanetetrayl tetrakis-(3,5-di-tert-butyl-4-hydroxyl-hydrocinnamate), di-n-octadecyl 3,5-di-tert- butyl-4-hydroxybenzylphosphonate, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, thiodiethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl)benzene, 3,6-di-oxaoctamethylene bis(3-methyl-5-tert-butyl-4-hydroxyhydrocinnamate), 2,6-di-tert-butyl-p-cresol, 2,2'-ethylidene-bis(4,6-di-tert-butylphenol), 1,3,5-tris(2,6-di-methyl-4-tert-butyl-3-hydroxybenzyl)isocyanurate, 1,1,3-tris-(2-methyl-4-hydroxy-5-tert-butylphenyl)butane, 1,3,5-tris-[2-(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyloxy)-ethyl]-isocyanurate, 3,5-di-(3,5-di-tert-butyl-4-hydroxybenzyl)-mesitol, hexamethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), 1-(3,5-di-tert-butyl-4-hydroxyanilino)-3,5-di(octylthio)-s-triazine, N,N'-hexamethylene-bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamamide), calcium bis(ethyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonate), ethylene bis[3,3-di(3-tert-butyl-4-hydroxyphenyl)butyrate], octyl 3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate, bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hydrazide, and N,N'-bis[2-(3,5-tert-butyl-4-hydroxyhydroxo-cinnamoyloxy)-ethyl]-oxamide, and preferably neopentanetetrayl tetrakis(3,5-di-tert-butyl-4 b 4-hydroxyhydrocinnamate), n-octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris-(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, 2,6-di-tert-butyl-p-cresol or 2,2'-ethylidene-bis(4,6-di-tert-butylphenol).

Likewise, the instant compounds prevent color formation when hindered amine light stabilizers are present, such hindered amines including bis(1,2,2,6,6-pentamethyl-4-piperidyl)-2-n-butyl-2-(3,5-di-tert-butyl-4-hydroxybenzyl) malonate; bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate; dimethylsuccinate polymer with 4-hydroxy-2,2,6,6-tetramethyl-1-piperidinethanol; and polymer of 2,4-dichloro-6-octylamino-s-triazine with N'-(2,2,6,6-tetramethyl-4-piperidyl)hexamethylene diamine.

The following examples illustrate the embodiments of this invention. Thus, they describe the preparation of various silanes and of stabilized compositions. In these examples, all parts given are by weight unless otherwise specified.

EXAMPLE I Trimethyl mono(N,N-dibenzylaminoxy)silane

A suspension of 15.93 g of dibenzylhydroxylamine in 100 ml of acetonitrile is admixed with 25.0 g of bis(trimethylsilyl)trifluoroacetamide with stirring. The mixture is heated at 80° C. under nitrogen for 30 minutes, and then cooled to room temperature and stirred for 8 hours. The solvent is removed under reduced pressure and the residue is distilled to afford the title compound as a colorless liquid.

Anal. Calcd. for C₁₇ H₂₃ NOSi: C, 71.5; H, 8.1; N, 4.9. Found: C, 70.8; H, 7.8; N, 5.2.

EXAMPLE II Dimethyl di(N,N-dibenzylaminoxy)silane

A solution of 21.23 g of dibenzylhydroxylamine and 20.9 ml of triethylamine in 200 ml of methylene chloride is admixed with a solution of 6.1 ml of dimethyldichlorosilane in 50 ml of methylene chloride. The solvent is removed under reduced pressure and the residue treated with heptane and the insoluble triethylaminehydrochloride removed by filtration. The heptane solution is concentrated under reduced pressure and the residue is triturated with methanol to afford the title compound; mp 50°-53° C.

Anal Calcd. for C₃₀ H₃₄ N₂ O₂ Si: C, 74.7; H, 7.1, N, 5.8. Found: C, 74.8; H, 7.1; N, 5.8.

EXAMPLE III Tetra[N,N-diethylaminoxy]silane

A solution of 17.0 g of silicontetrachloride in 200 ml of heptane is admixed with a solution of 73.1 g of diethylhydroxylamine in 50 ml of heptane. The reaction mixture is stirred at 55° C. for 2 hours and then cooled to 10° C. and the insoluble salt removed by filtration. The filtrate is concentrated under reduced pressure and distilled to yield the title compound as a pale yellow liquid.

Anal. Calcd. for C₁₆ H₄₀ N₄ O₄ Si: C, 50.5; H, 10.6; N, 14.7. Found: C, 50.4; H, 10.6, N, 14.6.

Example IV Processing of Polypropylene Base Formulation

Polypropylene*: 100 parts

Calcium Stearate: 0.10 part

The indicated stabilizers are solvent blended into polypropylene as solutions in methylene chloride and after removal of solvent by evaporation at reduced pressure, the resin is extruded using the following extruder conditions:

    ______________________________________                                                     Temperature (°C.)                                           ______________________________________                                         Cylinder #1   232                                                              Cylinder #2   246                                                              Cylinder #3   260                                                              Gate #1       260                                                              Gate #2       260                                                              Gate #3       260                                                              RPM           100                                                              ______________________________________                                    

During extrusion, the internal extruder pressure is determined using a pressure transducer. After each of the first, third and fifth extrusions, resin pellets are compression molded into 125 mil(b 3.2 mm) thick plaques at 193° C. and specimen yellowness index (Y.I.) determined according to ASTM D1925-63T.

The melt flow rate (MFR) is determined by ASTM method 1238 condition L. The melt flow rate varies inversely as the transducer pressure and both are a measure of the molecular weight for a specific type of polymer. The results are shown in the following table.

    ______________________________________                                         Series 1                                                                                  YI Color    MFR (g/10 min.)                                                    After Extrusion                                                                            After Extrusion                                         Additives    1      3      5     1     5                                       ______________________________________                                         Base Resin   2.5    3.5    4.7   6.3   14.9                                    0.1% Antioxidant A                                                                          7.4    13.2   15.9  3.4   6.9                                     0.1% Antioxidant A +                                                                        2.0    2.5    3.0   3.2   3.8                                     0.05% Ex. II                                                                   ______________________________________                                    

    ______________________________________                                         Series 2                                                                                  YI Color    MFR (g/10 min.)                                                    After Extrusion                                                                            After Extrusion                                         Additives    1       3     5     1     5                                       ______________________________________                                         Base Resin   1.8     2.5   3.5   5.0   9.9                                     0.1% Antioxidant A                                                                          4.6     8.9   10.9  2.8   4.8                                     0.1% Antioxidant A +                                                                        2.7     4.2   4.8   2.3   3.2                                     0.05% Ex. III                                                                  ______________________________________                                    

    ______________________________________                                         Series 3                                                                                    YI Color                                                                       After Extrusion                                                                1         3      5                                                ______________________________________                                         Base Resin     -3.5        -3.4   -2.7                                         0.1% Antioxidant A                                                                            -1.1         1.4    3.8                                         0.1% Antioxidant A +                                                                          -3.9        -2.9   -1.6                                         0.05% Ex. I                                                                    ______________________________________                                          Antioxidant A  Neopentyl tetrakis                                              [3(3',5di-tert-butyl-4hydroxyphenyl)propanoate                           

EXAMPLE V Light Stabilization of Polypropylene

Unstabilized polypropylene powder (Hercules Profax 6501) is thoroughly blended with the indicated amount of additive. The blended materials are then milled on a two-roll mill at 182° C. for 5 minutes, after which time the stabilized polypropylene is sheeted from the mill and allowed to cool. The milled polypropylene is then cut into pieces and compression molded on a hydraulic press at 250° C. and 175 psi (1.2×10⁶ Pa) into 25 mil plaques. The sample is exposed in a fluorescent sunlight/black light chamber until failure. Failure is taken as the hours required to reach 0.5 carbonyl absorbance by infrared spectroscopy on the exposed films.

    ______________________________________                                                     Additive                                                           Additive    Conc.       FS/BL Test Results                                     Compound of (% by weight)                                                                              (Hours to Failure)                                     ______________________________________                                         --          --          100                                                    Example I   0.2         250                                                    ______________________________________                                    

These data in Examples IV and V thus indicate the effective stabilization and color improving activity of the instant compounds.

Summarizing, it is seen that this invention provides organic materials stabilized against degradation by the presence therein of various aminoxy silanes. Variations may be made in proportions, procedures and materials without departing from the scope of the invention as defined by the following claims. 

What is claimed is:
 1. A composition of matter comprising an organic material selected from the group consisting of polymers devoid of silicon atoms, naturally occuring and synthetic mineral oils, animal and vegetable fats, oils and waxes and synthetic ester-based oils, fats and waxes subject to oxidative, thermal and actinic degradation stabilized with an effective stabilizing amount of a compound of the formula ##STR3## wherein n is 0-4; and R, R¹ and R² are independently hydrogen, alkyl of 1 to 36 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, aralkyl of 7 to 9 carbon atoms or said aralkyl substituted by alkyl of 1 to 36 carbon atoms.
 2. The composition of claim 1, wherein R¹ and R² are independently hydrogen, straight-chain or branched alkyl of 1 to 18 carbon atoms, cyclopentyl, cyclohexyl, benzyl, α-methylbenzyl or α,α-dimethylbenzyl.
 3. The composition of claim 2, wherein R¹ and R² are benzyl.
 4. The composition of claim 1, wherein R is C₁ -C₁₈ alkyl.
 5. The composition of claim 2, wherein said compound is trimethyl mono(N,N-dibenzylaminoxy)silane.
 6. The composition of claim 2, wherein said compound is dimethyl di(N,N-dibenzylaminoxy)silane.
 7. The composition of claim 2, wherein said compound is tetra[N,N-diethylaminoxy]silane.
 8. The composition of claim 1, wherein the organic material is a synthetic polymer.
 9. The composition of claim 8, wherein said synthetic polymer is a polyolefin homopolymer or copolymer.
 10. The composition of claim 9 which also contains a metal salt of a higher fatty acid.
 11. The composition of claim 1, which also contains a phenolic antioxidant.
 12. The composition of claim 10 which also contains a phenolic antioxidant.
 13. The composition of claim 11, wherein said phenolic antioxidant is selected from the group consisting of n-octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, neopentanetetrayl tetrakis-(3,5-di-tert-butyl-4-hydroxylhydrocinnamate), di-n-octadecyl 3,5-di-tert-butyl-4-hydroxybenzyl-phosphonate, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxy-benzyl)isocyanurate, thiodiethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl)benzene, 3,6-di-oxaocta-methylene bis(3-methyl-5-tert-butyl-4-hydroxyhydro-cinnamate), 2,6-di-tert-butyl-p-cresol, 2,2'-ethylidene-bis(4,6-di-tert-butylphenol), 1,3,5-tris(2,6-di- methyl-4-tert-butyl-3-hydroxybenzyl)isocyanurate, 1,1,3-tris-(2-methyl-4-hydroxy-5-tert-butylphenyl)butane, 1,3,5-tris-[2-(3,5-di-tert-butyl-4-hydroxyhydro-cinnamoyloxy)-ethyl]-isocyanurate, 3,5-di-(3,5-di-tert-butyl-4-hydroxybenzyl)-mesitol, hexamethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), 1-(3,5-di-tert-butyl-4-hydroxyanilino)-3,5-di(octylthio)-s-triazine, N,N'-hexamethylene-bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamamide), calcium bis(ethyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate), ethylene bis[3,3-di(3-tert-butyl-4-hydroxyphenyl)butyrate], octyl 3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate, bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hydrazide, and N,N'-bis[2-(3,5-tert-butyl-4-hydroxyhydroxocinnamoyloxy)ethyl]oxamide.
 14. The composition of claim 13, wherein said phenolic antioxidant is selected from the group consisting of neopentanetetrayl tetrakis(3,5-di-tert-butyl-4-hydroxy hydrocinnamate), n-octadecyl 3,5-di-tert-butyl-4-hydroxy hydrocinnamate, 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris-(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, 2,6-di-tert-butyl-p-cresol and 2,2'-ethylidene-bis(4,6-di-tert-butylphenol).
 15. A method for stabilizing an organic material selected from the group consisting of polymers devoid of silicon atoms, naturally occuring and synthetic mineral oils, animal and vegetable fats, oils and waxes and synthetic ester-based oils, fats and waxes against oxidative, thermal and actinic degradation which comprises incorporating into said organic material an effective stabilizing amount of a compound of claim
 1. 